素材不良的 2379, SKD11
- Aug 30 Sat 2008 11:34
氫 裂 hydrogen induced cracking
- Aug 30 Sat 2008 11:02
晶界腐蝕 GB corrosion
AISI 420 stainless steel. Hardened in saltbath. Salt residue corroded its surface grain boundary over a humid mid-summer night.
- Aug 27 Wed 2008 17:59
Fracture Surfaces 破斷面 欣賞
黃色箭頭為裂口蔓延方向.
- Aug 14 Thu 2008 19:18
破裂起源奌Crack Initiation Site
- Jul 22 Tue 2008 20:58
CE_Meter Catalogue
- Jul 13 Sun 2008 11:00
高炉炉渣內的小鉄塊
廢鉄貴了, 高炉炉渣也被從中鋼與國外買來粹取其中含鉄的部份, 賣给鑄造廠熔解. 吳老師撿了一小塊看其金相組織如下: 過共晶成份的鉄水, 急冷, 所以以過共晶白鑄鐵形態出現. 凝固自外圍往內進行. 外圍碳濃度低, 沒有"初晶碳化物", 內部碳濃度高, 故滿佈"初晶碳化物".
- Jul 05 Sat 2008 09:56
Correcting C% Si% 調整 補正
- Jul 03 Thu 2008 21:44
420 J2 不銹鋼 低淬低回 輕蝕
50X
100X